Zirconia Ceramic is with higher density, higher hardness and wear resistance characteristics etc, especially its bending strenghth and fracture toughness are very much higher than other non metallic materials, the service life is 3-5times of alumina ceramics. zirconia ceramic is widely used in various industries.
The chemical properties are as follows :
Bending strenghth : 800 Mpa
Fracture toughness : 6-8 Mpa.m3/2
Density : 5.8-6.02 g/cm3
Thermal conductivity Coefficient : 2.5-3
Mon's Hardness Scale : 8.5
Crafted with high-quality ceramic material, Zirconia Guide Pipe Bar ceramic Roller offers exceptional strength and durability, ensuring long-lasting performance in the most demanding environments. Its round shape allows for seamless integration into various industrial processes, providing superior accuracy and reducing downtime. With its excellent thermal stability and resistance to corrosion, our Ceramic Round Bar is ideal for use in high-temperature and corrosive environments. Upgrade your machining capabilities with this innovative product and experience enhanced productivity and efficiency like never before.
Properties Of Different Zirconia Material
| Property | Item | 3Y-TZP White /Black | Mg-PSZ | Nano 3Y-TZP | |||
| Mechanical Characteristics | Color | Ivory/Black | - | Gold Yellow | - | BLUE | - |
| Density | 6.02 | g/cm3 | 5.7 | g/cm3 | 6.01 | g/cm3 | |
| Bending Strength | 800 | MPa | 450 | MPa | 1200 | MPa | |
| Compressive trength | 3000 | MPa | 2500 | MPa | 3000 | MPa | |
| Elastic Modulus | 200 | GPa | 250 | GPa | 220 | GPa | |
| Fracture Toughness | 8 | MPa m1/2 | 6~7 | MPa m1/2 | 14 | MPa m1/2 | |
| Weber Coefficient | 15 | m | 12 | m | 25 | m | |
| Vickers Hardness | 1200 | HV 0.5 | 1100 | HV 0.5 | 1200 | HV 0.5 | |
| Thermal Characterics | Coefficient of Line Thermal Expansion | 10 | 10-6K-1 | 10 | 10-6K-1 | 10 | 10-6K-1 |
| Thermal Conductivity | 3 | W/mK | 3 | W/mK | 2 | W/mK | |
| Thermal Shock Resistance(Put in Water) | 300 | ΔT °C | 450 | ΔT °C | 300 | ΔT °C | |
| Max Working Temperature | 1000 | °C | 2100 | °C | 1000 | °C | |
| Electrical Characteristics | Volume Resistance at 20°C | >1013 | Ωcm | >1014 | Ωcm | >1013 | Ωcm |
| Dielectric Strength | 11×106 | V/m | 13 × 105 | V/m | 11×106 | V/m | |
| Dielectric Constant | 33 | εr | 28 | εr | 33 | εr | |
| One MHZ Dielectric Loss Angle at 20°C | 0.0016 | tanδ | 0.0017 | tanδ | 0.0016 | tanδ | |
| Chemical Characteristics | Nitric Acid (60%) 90°C | ≒0.00 | WT Loss mg/cm2/day | 0.1 | WT Loss mg/cm2/day | ≒0.00 | WT Loss mg/cm2/day |
| Sulphuric Acid (95%) 95°C | 0.04 | 0.34 | 0.03 | ||||
| Caustic Soda (30%) 80°C | 0.08 | 0.95 | 0.06 | ||||
This data is the result of laboratory testing. Customers need to judge whether it can be used according to the specific environment. | |||||||
Zirconia Guide Pipe Bar ceramic Roller
Zirconia Ceramic is with higher density, higher hardness and wear resistance characteristics etc, especially its bending strenghth and fracture toughness are very much higher than other non metallic materials, the service life is 3-5times of alumina ceramics. zirconia ceramic is widely used in various industries.
The chemical properties are as follows :
Bending strenghth : 800 Mpa
Fracture toughness : 6-8 Mpa.m3/2
Density : 5.8-6.02 g/cm3
Thermal conductivity Coefficient : 2.5-3
Mon's Hardness Scale : 8.5
Crafted with high-quality ceramic material, Zirconia Guide Pipe Bar ceramic Roller offers exceptional strength and durability, ensuring long-lasting performance in the most demanding environments. Its round shape allows for seamless integration into various industrial processes, providing superior accuracy and reducing downtime. With its excellent thermal stability and resistance to corrosion, our Ceramic Round Bar is ideal for use in high-temperature and corrosive environments. Upgrade your machining capabilities with this innovative product and experience enhanced productivity and efficiency like never before.
Properties Of Different Zirconia Material
| Property | Item | 3Y-TZP White /Black | Mg-PSZ | Nano 3Y-TZP | |||
| Mechanical Characteristics | Color | Ivory/Black | - | Gold Yellow | - | BLUE | - |
| Density | 6.02 | g/cm3 | 5.7 | g/cm3 | 6.01 | g/cm3 | |
| Bending Strength | 800 | MPa | 450 | MPa | 1200 | MPa | |
| Compressive trength | 3000 | MPa | 2500 | MPa | 3000 | MPa | |
| Elastic Modulus | 200 | GPa | 250 | GPa | 220 | GPa | |
| Fracture Toughness | 8 | MPa m1/2 | 6~7 | MPa m1/2 | 14 | MPa m1/2 | |
| Weber Coefficient | 15 | m | 12 | m | 25 | m | |
| Vickers Hardness | 1200 | HV 0.5 | 1100 | HV 0.5 | 1200 | HV 0.5 | |
| Thermal Characterics | Coefficient of Line Thermal Expansion | 10 | 10-6K-1 | 10 | 10-6K-1 | 10 | 10-6K-1 |
| Thermal Conductivity | 3 | W/mK | 3 | W/mK | 2 | W/mK | |
| Thermal Shock Resistance(Put in Water) | 300 | ΔT °C | 450 | ΔT °C | 300 | ΔT °C | |
| Max Working Temperature | 1000 | °C | 2100 | °C | 1000 | °C | |
| Electrical Characteristics | Volume Resistance at 20°C | >1013 | Ωcm | >1014 | Ωcm | >1013 | Ωcm |
| Dielectric Strength | 11×106 | V/m | 13 × 105 | V/m | 11×106 | V/m | |
| Dielectric Constant | 33 | εr | 28 | εr | 33 | εr | |
| One MHZ Dielectric Loss Angle at 20°C | 0.0016 | tanδ | 0.0017 | tanδ | 0.0016 | tanδ | |
| Chemical Characteristics | Nitric Acid (60%) 90°C | ≒0.00 | WT Loss mg/cm2/day | 0.1 | WT Loss mg/cm2/day | ≒0.00 | WT Loss mg/cm2/day |
| Sulphuric Acid (95%) 95°C | 0.04 | 0.34 | 0.03 | ||||
| Caustic Soda (30%) 80°C | 0.08 | 0.95 | 0.06 | ||||
This data is the result of laboratory testing. Customers need to judge whether it can be used according to the specific environment. | |||||||